hot sale factory 17-4 17-7 630 631 inox wear ring factory best price

Grade

C

Mn

Si

P

S

Cr

Mo

Ni

N

304

min.

max.

-

0.08

-

2.0

-

0.75

-

0.045

-

0.030

18.0

20.0

-

8.0

10.5

-

0.10

304L

min.

max.

-

0.030

-

2.0

-

0.75

-

0.045

-

0.030

18.0

20.0

-

8.0

12.0

-

0.10

304H

min.

max.

0.04

0.10

-

2.0

-

0.75

-0.045

-

0.030

18.0

20.0

-

8.0

10.5

-

Grade

Tensile Strength 

(MPa) min

Yield Strength 

0.2% Proof (MPa) min

Elongation (% in 50mm) min

Hardness

Rockwell B (HR B) max

Brinell (HB) max

304

515

205

40

92

201

304L

485

170

40

92

201

304H

515

205

40

92

201

304H also has a requirement for a grain size of ASTM No 7 or coarser.

Grade

Why it might be chosen instead of 304

301L

A higher work hardening rate grade is required for certain roll formed or stretch formed components.

302HQ

Lower work hardening rate is needed for cold forging of screws, bolts and rivets.

303

Higher machinability needed, and the lower corrosion resistance, formability and weldability are acceptable.

316

Higher resistance to pitting and crevice corrosion is required, in chloride environments

321

Better resistance to temperatures of around 600-900°C is needed…321 has higher hot strength.

3CR12

A lower cost is required, and the reduced corrosion resistance and resulting discolouration are acceptable.

430

A lower cost is required, and the reduced corrosion resistance and fabrication characteristics are acceptable.